For more information Manufacturers (Origin): Taiwan Country Joe Grade: D-120N Sales: Brand Distribution Type: standard material processing levels: extrusion grade level characteristics: Standard Use level: General Purpose Performance Project Test Conditions Test Method Value / Description Unit Mechanical properties of tensile strength (tensile strength) ASTM D638 / ISO 527 425-41.7 kg / cm? (MPa) [Lb / in2] Elongation at break ASTM D638 / ISO 527% tensile modulus ASTM D638 / ISO 527 kg / cm? (MPa) [Lb / in2] Tensile yield elongation (elongation) ASTM D638 / ISO 527% tensile elongation at break (elongation) ASTM D638 / ISO 527% flexural modulus (flexural modulus ) ASTM D790 / ISO 178 20800-2042 kg / cm? (MPa) [Lb / in2] bending strength ASTM D790 / ISO 178 705-69.2 kg / cm? (MPa) [Lb / in2] Rockwell hardness ASTM D785 104 IZOD notched impact strength 1/4 "23 ℃ ASTM D256 / ISO 179 39 kg · cm / cm (J / M) ft · lb / in 1/4" -30 ℃ ASTM D256 / ISO 179 kg · cm / cm (J / M) ft · lb / in 1/8 "23 ℃ ASTM D256 / ISO 179 46 kg · cm / cm (J / M) ft · lb / in 1/8" -30 ℃ ASTM D256 / ISO 179 kg · cm / cm (J / M) ft · lb / in Charpy impact strength 23 ℃ (notched) ASTM D256 / ISO 179 kg · cm / cm (J / M) ft · lb / in -30 ℃ (notched) ASTM D256 / ISO 179 kg · cm / cm (J / M) ft · lb / in 23 ℃ (unnotched) ASTM D256 / ISO 179 kg · cm / cm (J / M) ft · lb / in -30 ℃ (unnotched) ASTM D256 / ISO 179 kg · cm / cm (J / M) ft · lb / in physical property specific gravity (density) ASTM D792 / ISO 1183 1.03 Molding shrinkage ASTM D955% melt index (flow coefficient) 200 ℃ / 5kg ASTM D1238 / ISO 1133 1.4 g / 10min 220 ℃ / 10kg ASTM D1238 / ISO 1133 8 g / 10min water absorption of 23 ℃ / 24H ASTM D570 / ISO 62% Thermal heat distortion temperature annealing ASTM D648 / ISO 75 88 ℃ (℉) without annealing ASTM D648 / ISO 75 90-194 ℃ (℉) Vicat softening point ASTM D1525 / ISO R306 ℃ (℉) melting point - ℃ (℉) Flammability (rate) UL94 HB linear expansion coefficient ASTM D696 / ISO 11359 mm / mm ℃ processing. dried conditions, processing temperature nozzle barrel front ℃ ℃ ℃ barrel after barrel in the middle segment ℃ melt temperature ℃ mold temperature ℃ pressure holding pressure injection pressure Mpa Mpa Mpa back pressure screw speed rpm Additional notes color characteristics suitable for extrusion / thermoforming, finished with extremely good surface, and due to the good resistance to stress creep properties, more suitable for the printing process and the production system of food packaging containers. Because of the intensity with excellent dimensional stability and is especially suitable for large-scale production system objects. Use extrusion grade, can be injection