Manufacturers (Origin): Taiwan Chemical Fiber Grade: AG1000 Sales: Brand Distribution Type: standard material processing level: injection grade level characteristics: high impact Use levels: General level data Performance Project test conditions [state] method of test data unit proportion ASMT D-792 (ISO 1183) 1.03 23 ℃ / 23 ℃ Flammability FILE NO. E162823 UL-94 HB melt flow rate 220 ℃ × 10kg ASTM D-1238 (ISO 1133) 10 g / 10min melt flow rate of 200 ℃ × 5kg ASTM D-1238 (ISO 1133) 0.4 g / 10min LZOD impact strength 23 ℃ 1/4 "thick ASTM D-256 (ISO R180) 40 (392) kg.cm/cm(J/m) Rockwell hardness 23 ℃ ASTM D-785 (ISO 2039/2) R-95 Flexural Modulus 23 ℃ ASTM D-790 (ISO 178) 19500 (1910) kg / cm2 (MPa) Bending strength 23 ℃ ASTM D-790 (ISO 178) 580 (57) kg / cm2 (MPa) Tensile strength 23 ℃ ASTM D-638 (ISO 527) 390 (38) kg / cm2 (MPa) Heat distortion temperature Annealed (8 ℃ × 8hr) ASTM D-648 (ISO 75 / A) 98 ℃ Vicat softening point 1KG load ASTM D-1525 (ISO 306) 101 ℃ heat distortion temperature Unanneaied 18.6kg / cm (1/2 "thick) ASTM D-648 (ISO 75 / A) 86 ℃